Solar Backsheet Directory

Welcome to the world’s most advanced solar backsheet product directory. Panel manufacturers can use our advanced technical filters to find the exact solar backsheet that match their needs. We have collated backsheet data from manufacturers from all around the world into a common template, allowing you to compare and review backsheets easily. Finally, please also note that on the left side of the page you can select the backsheet layer materials you are looking for.

Browse by

Region

Outer(Air)Layer

Mid Layer

Inner(Cell)Layer

Tensile Strength(Width/TD) ≥

Mpa

Interlayer Peel Strength ≥

N/cm

Thermal Shrinkage(Width/TD) ≤

%

Elongation(Length/MD) ≥

%

Elongation(Width/TD) ≥

%

Partial Discharge Voltage ≥

VDC

Breakdown Voltage ≥

kV

MVTR ≤

g/m2 per day

Width ≥

mm

Weight ≤

g/m2

Solar Backsheet Directory
(108 Individual Backsheet Models)

Backsheet Filters
µm µm
MPa MPa
%
N/cm N/cm
  • Solmate® TPT
    Series: Solmate® TPT
    Taiflex Scientific
    From $7.50 / m2
    Layers: Tedlar(PVF) / PET / Tedlar(PVF) Tensile Strength: --
    Total Thickness: 350±35 µm Thermal Shrinkage ≤: --
    Region: Taiwan Taiwan    
    Solmate® TPT has great performance of hydrolysis resistance, better properties of electric insulation and breakdown voltage. Its excellent UV performance and water resistance make it applicable to crystalline silicon solar modules.
  • SP-FPE325
    Series: SP-FPE325
    HuiZhou Sinpo New Materials
    Layers: FEVE / PET / EVA Tensile Strength: 180 MPa
    Total Thickness: 325±5 µm Thermal Shrinkage ≤: 1 %
    Region: China China    
    SP-FPE325 has a width of 325±5µm. It has low Moisture-Vapor Transmission Rate and strong peeling strength with EVA. It is a series of backsheet without yellow discoloration,delamination, blister nor embrittlement.
  • FFC-JW 30 Transparent
    Series: FFC-JW 30 Transparent
    Jolywood (Suzhou) Sunwatt
    Layers: FFC / PET / FFC Tensile Strength: 120 MPa
    Total Thickness: 295±14.75 µm Thermal Shrinkage ≤: 1 %
    Region: China China    
    The FFC-JW30 Transparent series has a membrane-adhesive integrated structure (FFC/PET/FFC) with fluorine coated on both sides of the backsheet; it applies the technology of plasma chemical modification and Fluoro-Silicon surface grafting. The transparent backsheet passed 1500h's Damp-heat Testing (85℃ * 85%RH).
  • TPEw
    Series: TPEw
    Lucky Film
    From $3.80 / m2
    Layers: Tedlar(PVF) / PET / PE Tensile Strength: 110 MPa
    Total Thickness: 347±10 µm Thermal Shrinkage ≤: 1.5 %
    Region: China China    
    FPE-350B has high EVA adhesion performance. It can prevent the breaking and bubbles between the batteries and the backsheet. With the outstanding water vapor impediment nature, it also increase the service life of the batteries.
  • LBS-CFE
    From $6.00 / m2
    Layers: PVDF / PET / PE Tensile Strength: 70 MPa
    Total Thickness: -- Thermal Shrinkage ≤: 1.5 %
    Region: Korea Korea    
    The LBS-CFE was developed for PV module protection under severe weather condition at lower cost by LGC’s advanced material & adhesion technology solution. It has higher damp heat property and higher bonding with EVA.
  • SP-PE300
    Series: SP-PE300
    HuiZhou Sinpo New Materials
    Layers: PET / EVA Tensile Strength: 130 MPa
    Total Thickness: 300±5 µm Thermal Shrinkage ≤: 1 %
    Region: China China    
    SP-PE300 is a kind backsheet with high untraviolet exposure and weather resistance, without yellow discoloration, embrittlement nor delamination.
  • FFC-JW 30
    Series: FFC-JW 30
    Jolywood (Suzhou) Sunwatt
    Layers: FFC / PET / FFC Tensile Strength: 120 MPa
    Total Thickness: 300±15 µm Thermal Shrinkage ≤: 1 %
    Region: China China    
    The FFC-JW30 series has white backsheet which enjoys high reflective effect; Made-to-order backsheet with width under 1300mm is available. It applies the technology of plasma chemical modification and Fluoro-Silicon surface grafting.
  • FPE-350CH
    From $4.50 / m2
    Layers: ETFE / PET / PE Tensile Strength: 110 MPa
    Total Thickness: 342±10 µm Thermal Shrinkage ≤: 1 %
    Region: China China    
    FPE-350CH has strong anti-ultraviolet performance and weathering resistance. No need of special packing, standing storage. It is consistent with the current laminating process.
  • KPE
    Series: KPE
    Hangzhou Hongfu Technologies
    From $2.25 / m2
    Layers: PVDF / PE / EVA Tensile Strength: 120 MPa
    Total Thickness: 320±15 µm Thermal Shrinkage ≤: 0.95 %
    Region: China China    
  • PRESERV 1 - 225 WD/KD
    From $4.20 / m2
    Layers: PVDF / PET / Primer Tensile Strength: 115 MPa
    Total Thickness: 370 µm Thermal Shrinkage ≤: 1.5 %
    Region: India India