Type: | Fast Cure |
---|---|
Region: | China |
Product Characteristics | |
---|---|
Type | Fast Cure |
Thickness | 0.3-0.8 mm |
Width | ≤2150 mm |
Roll Length | 100 m |
VA Content | 33 % |
Melt Flow Index | 40 g/10min |
Density | 0.96 g/cm3 |
Stability Characteristics | |
Tensile Strength | 26 Mpa |
Young's Modulus | 4.7 Mpa |
Elongation | 550 % |
Water Absorption (20°C) | ≤0.01 % / day |
Peel Strength (Encapsulants-Glass) | ≥60 N/cm |
Peel Strength (Encapsulants-Backsheet) | ≥40 N/cm |
UV Aging (Light Transmittance) | ≤3 % |
Damp-Heat Aging (Light Transmittance) | ≤3 % |
Optical & Thermal Characteristics | |
Light Transmittance | ≥90 % |
UV Cut Off Wavelength | 360 nm |
Melting Point | 65 °C |
Processing Time | |
Vacuuming Time | 5-7 min |
Lamination Time | 8-18 min |
Curing Temperature | 145 °C |