Solar Backsheet Directory

Welcome to the world’s most advanced solar backsheet product directory. Panel manufacturers can use our advanced technical filters to find the exact solar backsheet that match their needs. We have collated backsheet data from manufacturers from all around the world into a common template, allowing you to compare and review backsheets easily. Finally, please also note that on the left side of the page you can select the backsheet layer materials you are looking for.

Browse by

Region

Outer(Air)Layer

Mid Layer

Inner(Cell)Layer

Tensile Strength(Width/TD) ≥

Mpa

Interlayer Peel Strength ≥

N/cm

Thermal Shrinkage(Width/TD) ≤

%

Elongation(Length/MD) ≥

%

Elongation(Width/TD) ≥

%

Partial Discharge Voltage ≥

VDC

Breakdown Voltage ≥

kV

MVTR ≤

g/m2 per day

Width ≥

mm

Weight ≤

g/m2

Solar Backsheet Directory
(113 Individual Backsheet Models)

Backsheet Filters
µm µm
MPa MPa
%
N/cm N/cm
  • dyMat PYE3000
    Layers: PET / PET / Primer Tensile Strength: --
    Total Thickness: 295±14.75 µm Thermal Shrinkage ≤: 1.5 %
    Region: Italy Italy    
  • FPF
    Series: FPF
    Shanghai Sosun New Energy Technology
    Layers: Coating / PET / Coating Tensile Strength: 150 MPa
    Total Thickness: 250±10 µm Thermal Shrinkage ≤: 1.5 %
    Region: China China    
  • KPF Cynagard 215A
    Layers: PVDF / PET Tensile Strength: 100 MPa
    Total Thickness: 300.5±30 µm Thermal Shrinkage ≤: 1.5 %
    Region: China China    
    (Fluro-skin ® ) one step filming technology. Using Fluorine resin mix with TiO2 and directly coated on PET. Then, you can see a white thin film formed – Fluro skin.It firmly adhere with PET without need to use adhesive chemical. – environmental friendly.
  • PRESERV 1 - 150 TF
    Layers: PET / Primer Tensile Strength: 100 MPa
    Total Thickness: 300 µm Thermal Shrinkage ≤: 1.5 %
    Region: India India    
  • PRESERV  A - 150  WN/KN
    Layers: PET / PET / Primer Tensile Strength: 100 MPa
    Total Thickness: 320 µm Thermal Shrinkage ≤: 1.5 %
    Region: India India    
  • PRESERV Cu - 250 WD
    Layers: PVDF / PET Tensile Strength: 100 MPa
    Total Thickness: 325 µm Thermal Shrinkage ≤: 0.5 %
    Region: India India    
  • PRESERV  1 - 100  WD/KD
    Layers: PVDF / PET / Primer Tensile Strength: 100 MPa
    Total Thickness: 245 µm Thermal Shrinkage ≤: 1.5 %
    Region: India India    
  • BEC-301
    Series: BEC-301
    Hangzhou First PV Material
    Layers: Coating / PET / Coating Tensile Strength: --
    Total Thickness: 280 µm Thermal Shrinkage ≤: --
    Region: China China    
  • dyMat PYE
    Layers: PET / PET / Primer Tensile Strength: --
    Total Thickness: 295±14.75 µm Thermal Shrinkage ≤: 1.2 %
    Region: Italy Italy    
  • AKALIGHT HBF 185 b
    Layers: PET / AL / PET / Primer Tensile Strength: --
    Total Thickness: 330 µm Thermal Shrinkage ≤: --
    Region: Germany Germany