Type: | Fast Cure |
---|---|
Region: | China |
Product Characteristics | |
---|---|
Type | Fast Cure |
Thickness | 0.2-1 mm |
Width | ≤1300 mm |
Melt Flow Index | 30 g/10min |
Density | 0.96 g/cm3 |
Gel Content | ≥85 % |
Stability Characteristics | |
Tensile Strength | 25.5 Mpa |
Elongation | 420 % |
Water Absorption (20°C) | ≤0.01 % / day |
Peel Strength (Encapsulants-Glass) | ≥30 N/cm |
Peel Strength (Encapsulants-Backsheet) | ≥40 N/cm |
Damp-Heat Aging (Yellowish Index) | ≤2 △YI |
Optical & Thermal Characteristics | |
Light Transmittance | ≥91 % |
Melting Point | 58 °C |
Specific Heat | 2.3 J/°C·g |
Processing Time | |
Vacuuming Time | 3-6 min |
Lamination Time | 3-16 min |
Curing Temperature | 145 °C |
Curing Time | 20 min |