Type: | Standard Cure |
---|---|
Region: | China |
Product Characteristics | |
---|---|
Type | Standard Cure |
Thickness | 0.30-0.80 mm |
Width | ≤2100 mm |
Roll Length | 100-200 m |
VA Content | 28-33 % |
Melt Flow Index | 15-30 g/10min |
Density | 0.95 g/cm3 |
Hardness (Shore A) | 65 |
Gel Content | ≥75 % |
Stability Characteristics | |
Tensile Strength | 25 Mpa |
Young's Modulus | 4.7 Mpa |
Elongation | 550 % |
Water Absorption (20°C) | ≤0.1 % / day |
Peel Strength (Encapsulants-Glass) | ≥80 N/cm |
Peel Strength (Encapsulants-Backsheet) | ≥50 N/cm |
Thermal Shrinkage (Length / MD) | ≤2 % |
Thermal Shrinkage (Width / TD) | ≤1 % |
Volume Resistivity | >1.15x10 ^15 Ω·cm |
UV Aging (Yellowish Index) | ≤1 △YI |
UV Aging (Light Transmittance) | ≤3 % |
Damp-Heat Aging (Yellowish Index) | ≤2 △YI |
Damp-Heat Aging (Light Transmittance) | ≤2 % |
Optical & Thermal Characteristics | |
Light Transmittance | ≥91 % |
UV Cut Off Wavelength | 360 nm |
Refractive Index | 1.481 |
Melting Point | 55 °C |
Specific Heat | 2.2 J/°C·g |
Processing Time | |
Vacuuming Time | 4-5 min |
Lamination Time | 6-12 min |
Curing Temperature | 135-150 °C |