Welcome to the world’s most advanced solar EVA product directory. Panel manufacturers can use our advanced technical filters to find the exact solar encapsulant that match their needs. We have collated EVA data from manufacturers from all around the world into a common template, allowing you to compare and review EVA films easily.
Type: | Standard Cure | Tensile Strength: | 10 MPa |
Thickness: | 0.40 ~ 0.90 mm | Thermal Shrinkage (Length / MD) ≤: | 3 % |
Region: | Turkey |
Anti-PID: Exceptional Protection Against Potential Induced Degradation.
High Insulation: Ensures Electrical Safety And Enhances Performance.
Outstanding Adhesion: Secures Solar Cells Firmly, Improving Longevity.
Cross-Linking Speed: Facilitates Quicker And More Efficient Manufacturing.
Type: | Standard Cure | Tensile Strength: | 16 MPa |
Thickness: | -- | Thermal Shrinkage (Length / MD) ≤: | 2 % |
Region: | China |
• Different types of EVA film available: highly transparent, high UV cutoff, and highly reflective white
• Excellent weather resistance against high temperature, high humidity, and ultraviolet radiation
• Good adhesion between glass and different types of back films
• Low shrinkage to ensure component stability during lamination
Type: | Fast Cure | Tensile Strength: | -- |
Thickness: | 0.40 ~ 0.60 mm | Thermal Shrinkage (Length / MD) ≤: | 5 % |
Region: | China |
White EVA increases PV module power efficiency remarkably
S201W‘s rough surface increases light diffuse reflection and PV module power efficiency
Excellent durability with good performance in DH & UV aging
Outstanding material compatibility and strong adhesive ability
Type: | Ultra Fast Cure | Tensile Strength: | 25 MPa |
Thickness: | 0.45 ~ 0.46 mm | Thermal Shrinkage (Length / MD) ≤: | 4 % |
Region: | China |
Excellent PID free properties
Superior weather-ability
Superior anti-Snail-Track performance
Excellent adhesion to glass and back sheet
UV Cut off for good light reflection
Type: | Fast Cure | Tensile Strength: | 10 MPa |
Thickness: | 0.2 ~ 0.8 mm | Thermal Shrinkage (Length / MD) ≤: | 3 % |
Region: | China |
Thermoplastic TPO adhesive film
Suitable for perovskite, CIGS, and lightweight components
Low laminate temperature short time
High weather resistance
Low water vapor transmittance
High transmittance
No small molecules are released
Type: | Fast Cure | Tensile Strength: | 18 MPa |
Thickness: | 0.2 ~ 1 mm | Thermal Shrinkage (Length / MD) ≤: | 3 % |
Region: | China |
Extra fast cure within 8 minutes
Low shrinkage, ensuring stable quality during lamination
Excellent adhesion between glass and different types of the back film
Excellent weather resistance (including high temperature, high humidity, and ultraviolet)
Type: | Standard Cure | Tensile Strength: | 12 MPa |
Thickness: | 0.40 ~ 0.90 mm | Thermal Shrinkage (Length / MD) ≤: | 3 % |
Region: | Turkey |
High Adhesion To Glass: Ensures A Secure Bond With Solar Panels.
Excellent Transparency: Maximizes Solar Energy Capture.
Strong Anti-PID Ability: Protects Against Performance Degradation.
UV Protection: Extends The Lifespan Of Solar Panels.
Low Water Vapor Rate: Minimizes Moisture Penetration.
Type: | Fast Cure | Tensile Strength: | -- |
Thickness: | 0.2 ~ 0.8 mm | Thermal Shrinkage (Length / MD) ≤: | 3 % |
Region: | China |
POE & EVA co-extruded adhesive film
Excellent water vapor barrier performance
Weather resistance
Higher cost advantage
Better anti-PID characteristics
Better peel strength retention
Type: | Fast Cure | Tensile Strength: | 25 MPa |
Thickness: | 0.5 ~ 0.6 mm | Thermal Shrinkage (Length / MD) ≤: | 4 % |
Region: | China |
1. Increase efficiency of PV modules markedly
2. Increasing light diffuse reflection
3. no white color overflow, no bubble, no cell string moving
4. Excellent durability, with good performance in DH&UV aging
5. Outstanding material compatibility. Strong adhesive ability with welding belt, cell, back sheet
Type: | Standard Cure | Tensile Strength: | 16 MPa |
Thickness: | -- | Thermal Shrinkage (Length / MD) ≤: | 2 % |
Region: | China |
• Different types of EVA film available: highly transparent, high UV cutoff, and highly reflective white
• Excellent weather resistance against high temperature, high humidity, and ultraviolet radiation
• Good adhesion between glass and different types of back films
• Low shrinkage to ensure component stability during lamination