Solar Panel EVA Directory
Welcome to the world’s most advanced solar EVA product directory. Panel manufacturers can use our advanced technical filters to find the exact solar encapsulant that match their needs. We have collated EVA data from manufacturers from all around the world into a common template, allowing you to compare and review EVA films easily. Finally, please also note that at the top of the page you can select the type of EVA you are looking for (Standard Cure, Fast Cure or Ultra Fast Cure).
Browse by
Region
Thermal Shrinkage (Width /TD) ≤
%
Peel Strength (EVA - Glass) ≥
N/cm
Peel Strength (EVA - Backsheet) ≥
N/cm
Elongation ≥
%
Width ≤
mm
Hardness (Shore A)
to
Gel Content ≥
%
Light Transmittance ≥
%
Melting Point
to
°C
Vacuuming Time
to
min
Lamination Time
to
min
Solar Panel EVA Directory
(113 Individual EVA Models)
EVA Filters
%
-
Type: Fast Cure Tensile Strength: 15 MPa Thickness: 0.43 ~ 0.47 mm Thermal Shrinkage (Length / MD) ≤: -- Region: India 
-
Type: Fast Cure Tensile Strength: 18 MPa Thickness: -- Thermal Shrinkage (Length / MD) ≤: -- Region: United States 
-
Type: Fast Cure Tensile Strength: 27 MPa Thickness: 0.35 ~ 0.36 mm Thermal Shrinkage (Length / MD) ≤: 3 % Region: China 
-
Type: Ultra Fast Cure Tensile Strength: 15 MPa Thickness: -- Thermal Shrinkage (Length / MD) ≤: -- Region: United States
-
Type: Ultra Fast Cure Tensile Strength: 15 MPa Thickness: -- Thermal Shrinkage (Length / MD) ≤: -- Region: United States
-
Type: Ultra Fast Cure Tensile Strength: -- Thickness: 10 ~ 200 mm Thermal Shrinkage (Length / MD) ≤: -- Region: China
-
Type: Fast Cure Tensile Strength: 16 MPa Thickness: 0.4 ~ 0.8 mm Thermal Shrinkage (Length / MD) ≤: 3.5 % Region: China
-
Type: Ultra Fast Cure Tensile Strength: 15 MPa Thickness: -- Thermal Shrinkage (Length / MD) ≤: -- Region: United States
-
Type: Fast Cure Tensile Strength: 12 MPa Thickness: 0.43 ~ 0.47 mm Thermal Shrinkage (Length / MD) ≤: -- Region: India
-
Type: Ultra Fast Cure Tensile Strength: 15 MPa Thickness: -- Thermal Shrinkage (Length / MD) ≤: -- Region: United States