HBL-EVA061

NJ Hongbaoli New Materials Co., Ltd.
Type: Fast Cure
Region: China China
Note: Your Enquiry will be sent directly to NJ Hongbaoli New Materials Co., Ltd..

Alternative Product

From $1.51 / m2
  • Thickness: 0.4275-0.4725 mm
  • TYPE: Fast Cure
  • Width: ≤1240 mm
  • Roll Length: --
  • VA Content: --
  • Tensile Strength: 15 Mpa
  • Young's Modulus: --
  • Elongation: --
  • Water Absorption (20°C): 0.1 %/day
  • Light Transmittance: ≥92 %
  • UV Cut Off Wavelength: 360 nm
  • Refractive Index: 1.48
  • Melting Point: 60-62 °C
  • Specific Heat: 2.5 J/°C·g

Product Characteristics

Product Characteristics  
Type Fast Cure
Thickness 0.3-0.8 mm
Width ≤2200 mm
Melt Flow Index 43.6 g/10min
Density 0.974 g/cm3
Hardness (Shore A) 70-80
Gel Content ≥80 %
Stability Characteristics  
Tensile Strength 25 Mpa
Young's Modulus 5.6 Mpa
Elongation 650 %
Water Absorption (20°C) ≤0.01 % / day
Peel Strength (EVA-Glass) ≥110 N/cm
Peel Strength (EVA-Backsheet) ≥80 N/cm
Thermal Shrinkage (Length / MD) ≤2 %
Thermal Shrinkage (Width / TD) ≤2 %
Volume Resistivity >1.48x10 ^6 Ω·cm
UV Aging (Yellowish Index) ≤2 △YI
Damp-Heat Aging (Yellowish Index) ≤4 △YI
Optical & Thermal Characteristics  
Light Transmittance ≥93 %
UV Cut Off Wavelength 360 nm
Refractive Index 1.486
Processing Time  
Vacuuming Time 3-5 min
Lamination Time 5-12 min
Curing Temperature 135 °C
Curing Time 15-20 min